AMS 5706 AMS5707 Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring
HomeHome > Products > Nickel Alloy > AMS 5706 AMS5707 Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring
AMS 5706 AMS5707 Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring

AMS 5706 AMS5707 Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring

AMS 5706 AMS 5544AMS5707 AMS5708 AMS5709 Nickel Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring Introduction Ha
Basic Info.
Model NO. Waspaloy
Technique Hot Rolled/Forged
Surface 2b/No.1
Stock in Stock
Key Words Haynes 25 Alloy Bar
Mtc En 10204 Type 3.1
MOQ 100kgs
Sample Free-Sample
Length Acc. to Requirement
Diameter 1-300mm
Transport Package Wooden Package
Specification haynes 188
Trademark ZYTC
Origin China
HS Code 7506200000
Production Capacity 50000kg/Month
Product Description

AMS 5706 AMS5707 Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring


AMS 5706 AMS5707 Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring

AMS 5706 AMS 5544AMS5707 AMS5708 AMS5709 Nickel Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring

Shape

Round,Forging,Ring,Coil,Flange,Disc,Foil,Spherical,Ribbon,Square,Bar,Pipe,Sheet

Grade

Duplex: 2205(UNS S31803/S32205),2507(UNS S32750),UNS S32760(Zeron 100),2304,904L

Others:253Ma,254SMo,654SMo,F50(UNSS32100)F60,F61,F65,1J22,N4,N6 etc

Alloy : Alloy 20/28/31

Hastelloy:HastelloyB/ -2/B-3/C22/C-4/S/ C276/C-2000/G-35/G-30/X/N/g

Hastelloy B / UNS N10001,Hastelloy B-2 / UNS N10665 / DIN W. Nr. 2.4617,Hastelloy C,

Hastelloy C-4 / UNS N06455 / DIN W. Nr. 2.4610,Hastelloy C-22 / UNS N06022 / DIN W. Nr. 2.4602,

Hastelloy C-276 / UNS N10276 / DIN W. Nr. 2.4819,Hastelloy X / UNS N06002 / DIN W. Nr. 2.4665

Haynes: Haynes 230/556/188

Inconel 600/601/602CA/617/625/713/718/738/X-750,Carpenter 20

Inconel 718 / UNS N07718 / DIN W. Nr. 2.4668,Inconel 601 / UNS N06601 / DIN W. Nr. 2.4851,

Inconel 625 / UNS N06625 / DIN W. Nr. 2.4856,Inconel 725 / UNS N07725,Inconel X-750 / UNS N07750 / DIN W. Nr. 2.4669,Inconel 600 / UNS N06600 / DIN W. Nr. 2.4816

Incoloy: Incoloy 800/800H/800HT/825/925/926;

GH: GH2132,GH3030,GH3039,GH3128,GH4180,GH3044

Monel: Monel 400/K500/R405

Nitronic: Nitronic 40/50/60;

Nimonic: Nimonic 75/80A/90/A263 ;

Specification

Wire: 0.01-10mm
Strip: 0.05*5.0-5.0*250mm
Bar: φ4-50mm;Length 2000-5000mm
Pipe: φ6-273mm;δ1-30mm;Length 1000-8000mm
Sheet: δ 0.8-36mm;Width 650-2000mm;Length 800-4500mm

Introduction

Haynes 188 is a cobalt-based alloy which possesses a unique combination of properties. It has excellent high temperature strength and oxidation resistance to 2100°F (1150°C) combined with good post-aging ductility.
Alloy 188 has average room temperature tensile properties in the bright annealed condition of 137.2 ksi (946 MPa) ultimate strength, 67.3 ksi (464 MPa) yield strength and 53% elongation. At 1800°F (980°C) the alloy has ultimate and yield strengths of 35.2 ksi (243 MPa) and 19.0 ksi (131 MPa), respectively, with 59% elongation. Cryogenic temperatures do not significantly affect the ductility of alloy 188, but strength levels are increased markedly.
The excellent oxidation resistance of Haynes 188 results from minute additions of lanthanum, which modifies the protective oxide scale in such a manner that the oxide becomes extremely tenacious and retards diffusion when exposed to temperatures through 2100°F (1150°C).
Haynes 188 exhibits good ductility after prolonged exposure at temperatures of 1200, 1400, and 1600°F (650, 760 and 870°C) for 16,000 hours.

Chemical Composition

The chemical composition of Haynes 188 is outlined in the following table.

Waspaloy (also known as Alloy 685) is a nickel base, age hardenable superalloy with excellent high-temperature strength and good corrosion resistance by combustion products, notably to oxidation, at service temperatures of up to 1200°F (650°C) for critical rotating applications, and up to 1600°F (870°C) for less demanding applications. At temperatures over 1600°F (870°C), intergranular oxidation can occur.

The corrosion resistance is very good even after numerous cycles of elevated temperature exposure, or constant exposure to temperatures of up to 1900°F (1038°C). For the best possible corrosion resistance, solution-treated material is recommended. Waspaloy is also known to behave well in atmospheres in gas turbine engine service and salt spray environments.

Due to these properties, Nickel Waspaloy finds use in gas turbine engine components and aircraft jet engines, such as compressor disks, rotor disks, shafts, spacers, seals, rings, and casings. It also finds use in fasteners and other engine hardware in airframe assemblies and missile systems. Waspaloy is produced by vacuum induction melting and vacuum arc refining (VIM/VAR), or by vacuum induction melting and electroslag refining (VIM/ESR).

Tech Steel & Materials offers Nickel Waspaloy in 8 sub-type specifications and in multiple shapes/forms:

  • AMS 5544 (Plate, Sheet, and Strip)
  • AMS 5586 (Tubing)
  • AMS 5704 (Forging)
  • AMS 5706 (Bar, Forging, and Ring)
  • AMS 5707 (Bar, Forging, and Ring)
  • AMS 5708 (Bar, Forging, and Ring)
  • AMS 5709 (Bar and Forging)
  • AMS 5828 (Wire)

Chemical Composition of Nickel Waspaloy

Chemical Composition of Nickel Waspaloy (Nominal Composition Alloy 685)
Elementminmax
Carbon0.020.10
Manganese0.10
Silicon0.15
Phosphorus0.015
Sulfur0.015
Chromium18.0021.00
Cobalt12.0015.00
Molybdenum3.505.00
Titanium2.753.25
Aluminum1.201.60
Zirconium0.020.08
Boron0.0030.010
Iron2.00
Copper0.10
Lead0.0005 (5 ppm)
Bismuth0.00003 (0.3 ppm)
Selenium0.0003 (3 ppm)
Silver0.0005 (5 ppm)
Nickel*remainder

*Not exclusively to the element mentioned, but that one predominates other elements that are used only in minimal quantities.

Fabrication and Working Instructions for Waspaloy

Waspaloy can be hot-worked in the temperature range of 2140-1800°F (1170-980°C), and cold-worked by hydroforming, drawing, spinning, bending, and rolling. That said, this nickel base alloy is difficult to machine and special instructions must be followed.

As for joining, Waspaloy can be readily-welded only in carefully controlled circumstances with argon-arc methods using the AMS 5828 composition filler metal. That said, welds should be avoided in high-stress locations, due to the fact that the high strength of the welds is lower than a heat-treated material. More precisely, Waspaloy may show "hot short" tendency and sensitivity to strain cracking. That's why, it is highly recommended that welding is done on a material that is only solution treated, and then re-solution treated together with the weld.

Physical Constants of Waspaloy (Alloy 685)

Density0.296 lb/in3
8.19 g/cm3
Melting Range2425-2475°F (1330-1360°C)
Coefficient of Thermal Expansionat 70-200°F (21-93°C) - 6.8 x 10-6 in/in/°F
at 70-1000°F (21-583°C) - 7.7 x 10-6 in/in/°F
at 70-2000°F (21-1093°C) - 10.4 x 10-6 in/in/°F
Electrical ResistivitySolution treated at 1975°F (1080°C) and cooled for 4 hours - 1.24 microhm•m (0.38 microhm•ft)
Fully age hardened at 1550°F (845°C), and cooled for 24 hours + reheat to 760°C (1400°F), and cooled for 16 hours - 1.20 microhm•m (0.37 microhm•ft)
Modulus of Elasticity (Dynamic)at 70°F (21°C) - 30.3 x 103 ksi (211 GPa)
at 1000°F (538°C) - 26.7 x 103 ksi (184 GPa)
at 1600°F (871°C) - 22.7 x 103 ksi (157 GPa)
Magnetic Permeability (200 oersteds)Solution treated + aged - 1.004

Minimum Tensile Properties (Room Temp)

PropertyValue
Tensile Strength175 ksi
Yield Strength at 0.2% Offset120 ksi
Elongation in 4D15%
Reduction of Area18%

Heat Treating Nickel Waspaloy

Nickel Waspaloy is heat treated in a three-step sequence. There are two different treatments available, both giving different properties to the alloy:

For parts that require high-temperature creep and stress-rupture properties:

  • Solution treatment - heat at 1975°F (1080°C), and air cool for 4 hours to produce hardness of 20-25 Rockwell C;
  • Stabilization - reheat to 1550°F (845°C), and air cool for 24 hours;
  • Age harden - reheat to 1400°F (760°C), and air cool for 16 hours to achieve a hardness of 34-40 Rockwell C;

For parts that require optimum tensile properties at room temperature and high-temperature environments:

  • Solution treatment - heat at 1825-1895°F (995-1035°C), and then oil quench for 4 hours;
  • Stabilization - reheat to 1550°F (845°C), and air cool for 4 hours;
  • Age harden - reheat to 1400°F (760°C), and air cool for 16 hours to produce hardness of 33-44 Rockwell C;

Scale may be formed on the alloy during heat treatment in oxidizing atmospheres. However, this doesn't affect the properties of the alloy and can be removed by acid pickling or mechanically.

Select AMS Number:

AMS NumberAlloyTypeUNSCross Ref. SpecMisc./Shape
AMS 5544WaspaloyNickelN07001
AMS 5544 Waspaloy PlateWaspaloyNickelN07001-Waspaloy Plate
AMS 5544 Waspaloy SheetWaspaloyNickelN07001-Waspaloy Sheet
AMS 5544 Waspaloy StripWaspaloyNickelN07001-Waspaloy Strip
AMS 5586WaspaloyNickelN07001-Waspaloy Tubing
AMS 5704WaspaloyNickelN07001-Waspaloy Forging
AMS 5706WaspaloyNickelN07001
AMS 5706 Waspaloy BarWaspaloyNickelN07001-Waspaloy Bar
AMS 5706 Waspaloy ForgingWaspaloyNickelN07001-Waspaloy Forging
AMS 5706 Waspaloy RingWaspaloyNickelN07001-Waspaloy Ring
AMS 5707WaspaloyNickelN07001
AMS 5707 Waspaloy BarWaspaloyNickelN07001-Waspaloy Bar
AMS 5707 Waspaloy ForgingWaspaloyNickelN07001-Waspaloy Forging
AMS 5707 Waspaloy RingWaspaloyNickelN07001-Waspaloy Ring
AMS 5708WaspaloyNickelN07001
AMS 5708 Waspaloy BarWaspaloyNickelN07001-Waspaloy Bar
AMS 5708 Waspaloy ForgingWaspaloyNickelN07001-Waspaloy Forging
AMS 5708 Waspaloy RingWaspaloyNickelN07001-Waspaloy Ring
AMS 5709WaspaloyNickelN07001
AMS 5709 Waspaloy BarWaspaloyNickelN07001-Waspaloy Bar
AMS 5709 Waspaloy ForgingWaspaloyNickelN07001-Waspaloy Forging
AMS 5828WaspaloyNickelN07001-Waspaloy Wire

AMS 5706 AMS5707 Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring



AMS 5706 AMS5707 Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring


AMS 5706 AMS5707 Waspaloy Gh4738 Uns N07001 Nickel Alloy Bar Forging Ring



Q1: Do you accept the trial order ?
A1: Yes,if we have the exactly size in stock.we can delivery even 1 piece/meter .Q2: Can I have free sample before making orders?

A2: Yes,we can supply free sample as requirement,but buyer needs to pay the freight charges ,the freight fee will return to buyer after making order.Q3: How do you control the quality ?A3: MTC and PMI will be sent before shipment,any 3rd party inspection if need .Q4: How about your delivery time ?A4: Generally delivery time is 15 working days .Q5: How can I quickly get the price list ?A5: Directly click "chat now" or send us email with detail specifications,you will get the official price list in 1 hour .